Killed Steel
Steel deoxidized with a strong deoxidizing agent, such as silicon or aluminum, to reduce the oxygen content to such a level that no reaction occurs between carbon and oxygen during solidification.

Killed Steel
The term killed indicates that the steel has been sufficiently deoxidized to quiet the molten metal when poured into the ingot mold. The general practice is to use aluminum ferrosilicon or manganese as deoxidizing agents. A properly killed steel is more uniform as to analysis and is comparatively free from aging. However, for the same carbon and manganese content Killed Steel is harder than Rimmed Steel. In general all steels above 0.25% carbon are killed, also all forging grades, structural steels from 0.15% to 0.25% carbon and some special steels in the low carbon range. Most steels below 0.15% carbon are rimmed steel.

Killed Steel
Steel deoxidized with a strong deoxidizing agent such as silicon or aluminum in order to reduce the oxygen content to such a level that no reaction occurs between carbon and oxygen during solidification.

Kind Band (deformation)
In polycrystalline materials, a volume of crystal that has rotated physically to accommodate differential deformation between adjoining parts of a grain while the band itself has deformed homogeneously. This occurs by regular bending of the slip lamellae along the boundaries of the band.

Kip
A load of 1000 lbs.